Lanxess Durethan® DP 2802/30 000000 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 2802/30 000000 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66 injection molding grade, 30% glass fibers, UL 94V-2 at 0.75 mm , GWFI:960°C at 0.75 mm, GWIT: 775°C at 0,75 mm, halogen-freeApplication Examples: mixer insert for blenders, washing machine front
panels
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Viscosity Test | 127 cm³/g | 127 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0064 cm/cm | 0.0064 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm | 0.0077 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | ISO 527-1/-2 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Conditioned; ISO 527-1/-2 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| 13.2 % | 13.2 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 7.8 % | 7.8 % | Conditioned; ISO 527-1/-2 |
| Tensile Modulus | 3.90 GPa | 566 ksi | Conditioned; ISO 527-1/-2 |
| 6.00 GPa | 870 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C | 39.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66, MF,14-060,GF30; ISO 1043-PA GF FR(30) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 241 PC (Europe-Africa-Middle East)
- Momentive Performance Materials Addisilâ„¢ 470 E Healthcare Extrusion Grade Heat Cured Rubber
- Schmolz + Bickenbach Thermodur® 2367 Superclean Hot Work Die Steel
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
- Lubrizol ESTANE® ETE55DT3 Ester Based Thermoplastic Polyurethane (European Grade)
- Axiall EX1188B Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved