Lanxess Durethan® DP 2325 H3.0 000000 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 2325 H3.0 000000 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, non-reinforced, elastomer-modified, good heat-ageing resistance, extremely high notched impact strength even at dry state and at low temperatures
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.076 g/cc | 0.03887 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0021 cm/cm | 0.0021 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527-1/-2 |
| 49.0 MPa | 7110 psi | Conditioned; ISO 527-1/-2 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | Conditioned; ISO 527-1/-2 |
| 50.0 MPa | 7250 psi | ISO 527-1/-2 | |
| Elongation at Break | 50 % | 50 % | Nominal; ISO 527-1/-2 |
| 50 % | 50 % | Nominal, Conditioned; ISO 527-1/-2 | |
| 80 % | 80 % | ISO 527-1/-2 | |
| 290 % | 290 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 21 % | 21 % | ISO 527-1/-2 |
| 38 % | 38 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.700 GPa | 102 ksi | Conditioned; ISO 527-1/-2 |
| 1.80 GPa | 261 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 3900 | 3900 | Puncture maximum force (N); ISO 6603-2 |
| 5400 @Temperature -30.0 °C |
5400 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 50.0 J | 36.9 ft-lb | ISO 6603-2 |
| 60.0 J @Temperature -30.0 °C |
44.3 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 60.0 J @Temperature -30.0 °C |
44.3 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+19 ohm-cm | 1.00e+19 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 | |
| 7.0 @Frequency 100 Hz |
7.0 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| 45.0 kV/mm | 1140 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.075 @Frequency 1.00e+6 Hz |
0.075 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.15 @Frequency 100 Hz |
0.15 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| High impact or high impact modified | ||
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MPHR,-20 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Network Polymers NPP 1418
- Flint Hills AP5155-HA Polypropylene Impact Copolymer
- Global Atron 6601-B General Purpose Nylon 66
- Lucobit Lucofin® 1454 Polyolefin TPO Granules, Green
- Solvay Specialty Polymers Radel® R-7159 Polyphenylsulfone (PPSU)
- SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East)
- Borealis Supercure™ LE8201R Polyethylene Insulation Compound, Crosslinkable
- Adell EA-16 Homopolymer Polypropylene, 30% Talc Filled
- 3M Scotch-Weld™ 3747 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved