- Aclo Accuguard Polycarbonate POL050G10HIV0L Glass Reinforced High Impact Flame Retardant
Aclo Accuguard Polycarbonate POL050G10HIV0L Glass Reinforced High Impact Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polycarbonate POL050G10HIV0L Glass Reinforced High Impact Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD; ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 69.98 MPa | 10150 psi | ASTM D638 |
| Tensile Strength, Yield | 75.98 MPa | 11020 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.899 GPa | 420.5 ksi | ASTM D638 |
| Flexural Strength | 122.0 MPa | 17690 psi | ASTM D790 |
| Flexural Modulus | 3.699 GPa | 536.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | |
| Flammability, UL94 | V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
UL File #E99379 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1240MHL BK Nylon 6/6
- Karina E 813-10/164-B-RT-PO White PVC Compound
- Lehmann & Voss LUVOCOM® 1105-7709/RD PEEK, unreinforced
- Techmer ES HiFill® PA4/6 CF40 HS 40% Carbon Filled (Conditioned)
- Toho Tenax Besfight® G30-500 3K HTA-7C EP01 Continuous Filament Carbon Fiber
- Wieland 1925 Wilaform Palladium
- Hexcel® Redux® 119 Surface Pretreatment Protection Solution
- 3M Scotchcal™ 50-914 Graphic Film
- Beijing Ranger Chem PBT-MFC-G20 FR PBT
Copyright © lookpolymers.com All Rights Reserved