Lanxess Durethan® BKV 40H2.0 EF 900116 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 40H2.0 EF 900116 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 40% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0060 cm/cm | 0.0060 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 12.6 GPa | 1830 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 290 MPa @Strain 3.20 % |
42100 psi @Strain 3.20 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 12.1 GPa | 1750 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | 79.0 kJ/m² | 37.6 ft-lb/in² | d.a.m.; ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 86.0 kJ/m² | 40.9 ft-lb/in² | d.a.m.; ISO 180-1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1, -3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, GHR, 10-120, GF40 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable E1330I Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Maxxam™ PD 40 TF Black Polypropylene Homopolymer (PP Homopolymer)
- Kleerdex Kydex® P54 Acrylic/PVC Extrusion Compound (discontinued **)
- Gwent Electronic Materials P2121112P15 Ammonia Plasma Modified Single and Double Walled Carbon Nanotubes
- SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific)
- Zeon Chemicals Zetpol® 2030H Hydrogenated Nitrile Elastomomer
- A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
- Lubrizol ESTANE® GP80AB Ester Based Thermoplastic Polyurethane
- Covestro Makrolon® 6255 Polycarbonate
- Ensinger Tecatron® XP-81 Compression Molded PPS Compound, Filled with 15% Graphite and 15% Carbon Fiber
Copyright © lookpolymers.com All Rights Reserved