Lanxess Durethan® BKV 30 G H2.0 900051 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 G H2.0 900051 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 30% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 30 H2.0, heat-stabilized, good heat-ageing resistance, good UV stability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 6.5 % | 6.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm | 0.0027 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm | 0.0058 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
| 180 MPa | 26100 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 7.0 % | 7.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.20 GPa | 899 ksi | Conditioned; ISO 527-1/-2 |
| 9.50 GPa | 1380 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 838 | 838 | Puncture maximum force (N); ISO 6603-2 |
| 735 @Temperature -30.0 °C |
735 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.60 J | 1.92 ft-lb | ISO 6603-2 |
| 2.20 J @Temperature -30.0 °C |
1.62 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.20 J @Temperature -30.0 °C |
1.62 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 221 °C | 430 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Vicat Softening Point | 210 °C | 410 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
IEC 60250 | |
| 4.3 @Frequency 1.00e+6 Hz |
4.3 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 7.0 @Frequency 100 Hz |
7.0 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | Conditioned; IEC 60243-1 |
| 34.0 kV/mm | 864 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.050 @Frequency 1.00e+6 Hz |
0.050 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.13 @Frequency 100 Hz |
0.13 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-100,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2000STL Nylon 6 (Cond)
- Rogers Corporation Poron® 4701-30-25 Supported Urethane Foam, Very Soft, Supported with Clear Polyester Film
- ICO Polymers ICOFLOâ„¢ 510-5008 1200 Micron HDPE Powder
- Multibase Multi-Flex® TPE A 5521 BLK
- SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66
- Universal Wire Works 141 Nickel Alloy Welding Wire
- Ashley Polymers Ashlene® P1440 Polycarbonate, 40% Glass Reinforced
- Albis Plastics Cellulose Acetate Butyrate B901 (UV Inhibitor Added), 13% Plasticizer (discontinued **)
- Karina E 841-08/184-A-ERYB Beige PVC Compound
Copyright © lookpolymers.com All Rights Reserved