Lanxess Durethan® BKV 20 FN20 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 20 FN20 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 20% glass fibers, injection molding, halogen-free flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.315 g/cc
1.315 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0060 cm/cm
0.0060 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 6.10 GPa
885 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 150 MPa

@Strain 5.00 %
 21800 psi

@Strain 5.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 135 MPa

@Strain 3.50 %
 19600 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 5.70 GPa
827 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²
<= 4.76 ft-lb/in²
d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
d.a.m.; ISO 180-1U
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
ISO 75-1, -2
Vicat Softening Point 205 °C

@Load 5.10 kg
 401 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
Glow Wire Test 960 °C

@Diameter 0.800 mm
 1760 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 1.50 mm
 1760 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 3.00 mm
 1760 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V
d.a.m.; Solution A; UL 746A
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
260 °C
500 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.070 %
0.030 - 0.070 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GFHR, 12-060, GF20; ISO 1043-PA GF FR(30)