LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Office equipment internal parts.Features: Lubricated, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 133 MPa | 19300 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 50.8 mm Span, 1 mm/min; ASTM D790 |
| Flexural Modulus | 8.14 GPa | 1180 ksi | (50.8 mm Span) 1mm/min; ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.95 J/cm | 7.40 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 11.3 J | 8.33 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C @Thickness 3.18 mm |
421 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.18 mm |
410 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 360 - 421 °C | 680 - 790 °F | |
| Middle Barrel Temperature | 371 - 421 °C | 700 - 790 °F | |
| Front Barrel Temperature | 382 - 427 °C | 720 - 801 °F | |
| Nozzle Temperature | 377 - 421 °C | 711 - 790 °F | |
| Melt Temperature | 382 - 427 °C | 720 - 801 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | <= 24 hour | <= 24 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |
| Clamp Pressure | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | Suggested |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Radici Radilon® CST 38FL (cond.) Nylon 6/66
- Lanxess Durethan® B 38 FKA 000000 Nylon 6, Film Grade
- Lanxess Durethan® BKV 315 Z H2.0 901510 Nylon 6, 15% Glass Fiber
- Teknor Apex Fireguard® 910-LBF Polyvinyl Chloride, Flexible
- Universal Wire Works 80SB-2 Steel Welding Wire
- Dow Corning MOLYKOTE® 822M GREASE
- ELASTO UK Dryflex® 402501S SBS Based Material, 50A Hardness, Black
- BASF Neopolen® P 8225 K 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Conditioned)
- Axiall 8266 Rigid PVC, Extrusion, White
Copyright © lookpolymers.com All Rights Reserved