SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | ASTM D638 |
| 141 MPa | 20500 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D638 |
| 13.87 GPa | 2012 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 187 MPa | 27100 psi | ASTM D790 |
| 214 MPa | 31000 psi | ISO 178 | |
| Flexural Modulus | 9.34 GPa | 1350 ksi | ASTM D790 |
| 11.14 GPa | 1616 ksi | ISO 178 | |
| Izod Impact, Notched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 66.0 kJ/m² | 31.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 13.0 J | 9.59 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 147 x 10-8 mm³/N-M | 73.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 33.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 45.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 HI/1 PA66, improved strength
- Radici Radilon® A ECP3808 (cond.) Nylon 66
- Michelman® Hydrosize® U5-01 Polyurethane dispersion
- Multibase Multi-Flex® A 5001 E LC Black TPE Thermoplastic Elastomer
- Schott N-LAF7 Glass
- Silon Taborex TA 2343 HD Catalyst Masterbatch
- UBE 5021T Nylon 6/66 Monofilament (Drawing Ratio=4.8)
- Clariant Renol PC010-L FR Polycarbonate, Glass Reinforced, Flame Retardant
- Cheng Yu Plastic B610 PC/PBT
Copyright © lookpolymers.com All Rights Reserved