LG Chemical TR-558A ABS, Transparent, High Strength

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical TR-558A ABS, Transparent, High Strength.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electronic parts, OA machines, toys and others that require transparency and high impact strength. An Izod impact strength or falling dart impact strength of LG transparent ABS is relatively similar to that of general ABS, it is not easily cracked like SAN or PMMA resin in the condition of low impact energy. TR-558 series is good for applications requiring high stiffness.Since LG transparent ABS TR-558A has excellent transparency and property balance, it could easily be applied on the following products: Electric and electronic: Vacuum cleaner parts, air-conditioner panel, humidifier water tank, mixer housing, copier parts, telephone parts, computer housing, facsimile parts, printer panel, washing machine panel and cover, electric fan stand, TV front frame, windows of microwave ovens, calculators, semiconductor carrier boxOther Applications: Compact cases, cosmetic parts, tool handles, toys, stationeries, game machineInformation Provided by LG Chem
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ASTM D792
Melt Index of Compound 24 g/10 min

@Load 10.0 kg,
Temperature 220 °C
24 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ASTM D638
Elongation at Break 35 %
35 %
50 mm/min; ASTM D638
Flexural Yield Strength 81.4 MPa
11800 psi
15 mm/min; ASTM D790
Flexural Modulus 2.45 GPa
355 ksi
15 mm/min; ASTM D790
Izod Impact Notched 2.98 J

@Thickness 3.20 mm
2.20 ft-lb

@Thickness 0.126 in
ASTM D256
3.24 J

@Thickness 6.40 mm
2.39 ft-lb

@Thickness 0.252 in
ASTM D256
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ASTM D1003
Transmission, Visible 88 %
88 %
ASTM D1003
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying