- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- LG Chemical RX710 ABS, High Impact, Chemical Resistance to HCFC
LG Chemical RX710 ABS, High Impact, Chemical Resistance to HCFC
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical RX710 ABS, High Impact, Chemical Resistance to HCFC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, Chemical Resistance to HCFC, High ImpactApplication: Refrigerator Dispensor & HomebarCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 37 g/10 min @Load 10.0 kg, Temperature 220 °C |
37 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 38.2 MPa @Thickness 3.20 mm |
5550 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 % @Thickness 3.20 mm |
>= 5.0 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.20 mm |
270 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
5.51 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 5.88 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
11.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 91.0 °C @Load 5.00 kg |
196 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 230 °C | 374 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 250 °C | 392 - 482 °F | Injection Molding |
| Nozzle Temperature | 200 - 250 °C | 392 - 482 °F | Injection Molding |
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.490 - 0.981 MPa | 71.1 - 142 psi | Injection Molding |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nye Lubricants 605A (SO) Synthetic Oil
- Chevron Phillips HiD® 9055 HDPE Injection Molding Resin (discontinued **)
- Saint-Gobain Rulon® CJ Grade Bearing/Seal PTFE (discontinued **)
- Hogen HM1100 Tungsten-Based Metal
- ICE Al2O3 99.8
- SK Chemicals SKYPEL G140D General Grade
- Fainplast Compounds PH 90/AS Flexible PVC, Transparent Extrusion
- E-Polymers TEKAMID® H24M10 MF 10% Heat resistance Dimensional stability PA/ABS Alloy
Copyright © lookpolymers.com All Rights Reserved