SABIC Innovative Plastics Xenoy® 1105 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 1105 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT/PC blend, injection molding grade, non-reinforced, impact modified, excellent toughness at low temperatures, very good paintability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 250 °C |
16 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| 16 g/10 min @Load 5.00 kg, Temperature 250 °C |
16 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | ISO 868 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 |
| 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 | |
| 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 7.3 % | 7.3 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| 110 % | 110 % | Type I, 5 mm/min; ASTM D638 | |
| 116 % | 116 % | 50 mm/min; ISO 527 | |
| 120 % | 120 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| 4.2 % | 4.2 % | Type I, 50 mm/min; ASTM D638 | |
| 4.5 % | 4.5 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.98 GPa | 287 ksi | 5 mm/min; ASTM D638 |
| 2.01 GPa | 292 ksi | 50 mm/min; ASTM D638 | |
| 2.07 GPa | 300 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 74.0 MPa | 10700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.01 GPa | 292 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.55 J/cm | 14.1 ft-lb/in | ASTM D256 |
| 3.72 J/cm @Temperature -40.0 °C |
6.97 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 4.89 J/cm @Temperature -30.0 °C |
9.16 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.87 J/cm @Temperature -20.0 °C |
12.9 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| 6.95 J/cm @Temperature -10.0 °C |
13.0 ft-lb/in @Temperature 14.0 °F |
ASTM D256 | |
| 7.15 J/cm @Temperature 0.000 °C |
13.4 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 63.0 kJ/m² | 30.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| 34.0 kJ/m² @Temperature -40.0 °C |
16.2 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 51.0 kJ/m² @Temperature -30.0 °C |
24.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 6.20 J/cm² | 29.5 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 4.70 J/cm² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 122 °C | 252 °F | Rate B/50; ASTM D1525 |
| 122 °C | 252 °F | Rate B/50; ISO 306 | |
| 123 °C | 253 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 1.2cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® 266 Specialty, Transparent (discontinued **)
- Monmouth Rubber & Plastics Durafoamâ„¢ C41 Closed Cell Epichlorohydrin
- Unifrax Foamfrax® Isofoam Fiber Insulation
- Covestro Bayfill® EA 6003 Polyurethane Energy-Absorbing Semi-Rigid Foam, Recoverable Grade, MDI-based 2-Component Liquid System
- Eurotec® Tecomid® NB30 GR13 BK EF PA6, 13% glass fiber reinforced, black, suitable for electrostatic powder coating
- DuPont Teijin Films Mylar® ADS Polyester Film, 400 Gauge
- Aaron Industries AAROLENE® AVPS HIPS 100-3 MELT 14 Virgin HIPS Resin
- Total Xsene® XS10 Orange YCF HDPE, pipe
- NOVA Chemicals Sclair® 11J1 Octene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved