LG Chemical Lupox® HI2303 PBT+GF30%
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical Lupox® HI2303 PBT+GF30%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+GF30%, High ImpactApplication: IT/OA, E&E (Bobbin, Switch)CAS No. 9003-01-04, 65997-17-3, 24968-12-5 and 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.010 cm/cm <br>@Thickness 3.20 mm |
0.0030 - 0.010 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.2 MPa <br>@Thickness 3.20 mm |
13500 psi <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % <br>@Thickness 3.20 mm |
3.0 % <br>@Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 157 MPa <br>@Thickness 3.20 mm |
22800 psi <br>@Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 6.37 GPa <br>@Thickness 3.20 mm |
925 ksi <br>@Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
2.57 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C <br>@Thickness 6.40 mm |
374 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C <br>@Thickness 6.40 mm |
356 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Melt Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products T20P250-01 20% Talc Reinforced Polypropylene Copolymer, Black
- Unifrax Fiberfrax® Rigidizer™ Inorganic Liquid Hardener
- A. Schulman POLYFORT™ FPP 1605 Glass Reinforced Chemically Coupled Copolymer
- Goodfellow Aluminum 50/Nickel 50 Alloy
- A. Schulman POLYBATCH™ Treated Pine 60175U/4 Concentrate Based In LLDPE
- American Elements Samarium Nanoparticles
- Lubrizol Estane® AG 8451 Thermoplastic Polyurethane
- Denka VINYKON W4029 PVC, W grade for equipment cords, for heat resistance
- Osprey Metals 316L/MA Master Alloy Stainless Steel Powder (Grade 80% - 22)
Copyright © lookpolymers.com All Rights Reserved