| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 0815 HHT Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS with very high heat resistanceGood melt flow rate, good impact resistance, excellent surface appearance, good processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D 638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D 638 |
| Elongation at Break | 15 % | 15 % | ASTM D 638 |
| Flexural Modulus | 2.65 GPa | 384 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 0.000 °C |
1.87 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 1.30 J/cm @Temperature 23.0 °C |
2.44 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 121 °C @Load 5.00 kg |
250 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 130 °C @Load 0.999 kg |
266 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-25 Urethane Foam, Very Soft
- Cookson Group Plaskon® 150.401 Encapsulation Resin (discontinued **)
- Ineos H03SLME Polypropylene Homopolymer
- Tra-Con Tra-Bond F113SC BLK High Tg Fiber Optic Epoxy Adhesive
- 3M SJ5400 Protective Product, Molded Shapes
- A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6
- Aaron Industries AAROLENE® ARPP C 200-3 Polypropylene Compounded Resin
Copyright © lookpolymers.com All Rights Reserved