LG Chemical LUPOY SG5009FA PC/ABS/PMMA, Halogen Free Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Acrylic (PMMA) , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY SG5009FA PC/ABS/PMMA, Halogen Free Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, High Gloss, Anti-scratchApplication: IT&OA (Notebook PC housing)CAS: 103598-77-2, 9003-56-9, 9011-14-7 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.040 | 0.040 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.7 MPa @Thickness 3.20 mm |
9670 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 103 MPa @Thickness 3.20 mm |
14900 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.79 GPa @Thickness 3.20 mm |
405 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.834 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.56 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | |
| Flammability, UL94 | V-0 @Thickness >=1.20 mm |
V-0 @Thickness >=0.0472 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 270 °C | 446 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Front Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Nozzle Temperature | 235 - 270 °C | 455 - 518 °F | Injection Molding |
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 1.96 MPa | 142 - 284 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Osprey Metals 80/20 Ni Cr Powder (Grade 90% - 22)
- Lucas-Milhaupt Premabraze 131 Gold Based Brazing Alloy
- Techmer ES Luriblend® PC IM FR
- Samsung Cheil Industries Infino® CF-1070 PC, Unreinforced High Impact
- Trelleborg S565 Silicone Rubber
- Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled
- ConocoPhillips SUPER-STA M NLGI No.0
- Adell WR-37 33% Glass Reinforced PET
- China-Yixing Longly Refractories 75 Alumina Ceramic
Copyright © lookpolymers.com All Rights Reserved