LG Chemical LUPOY HI5002A PC/ABS, High Impact
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY HI5002A PC/ABS, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, General Purpose, High Flow, High ImpactApplication: E&E (housing)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm |
7970 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 70 % @Thickness 3.20 mm |
70 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 84.3 MPa @Thickness 3.20 mm |
12200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa @Thickness 3.20 mm |
299 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 5.59 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 10.5 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 6.40 mm |
219 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 265 °C | 446 - 509 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Front Barrel Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Nozzle Temperature | 235 - 285 °C | 455 - 545 °F | Injection Molding |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nanocyl EPOCYL™ NC R128-04 Master Batch Liquid Bisphenol-A Resin for Solvent Based Formulation Purposes: Dilution Factor 6
- SABIC Innovative Plastics LNP LUBRICOMP DFL32XXC PC
- Lushan LR-1D Halogen-Free Flame-Retardant Compatibilizer
- Materion Beryllium Copper Alloy 25 Rod and Bar; AT (TF00) Temper; up to 76 mm (UNS C17200)
- LATI Lapex R PPSU
- Techmer ES HiFill® HDPE GF25 CC 25% Glass Filled
- Teknor Apex APEX® 3311-75 Polyvinyl Chloride, Flexible
- Eagle Brass 18665 MSP1, Hard
- EMS-Griltech Grilamid® HP 1200 Nylon 12 Fiber (Staple Length = 51)
- BASF Ultradur B 4300 G3 15% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved