LG Chemical LUPOY HF-5000 High Flow PC/ABS Alloy, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY HF-5000 High Flow PC/ABS Alloy, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housingElectrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector, switchIndustrial Parts and Household Appliance: Helmet, terminal box, electrical tool housing, industrial bobbin, distributing board box, power tool component, gears and cams, water meter housingInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 2.155 GPa | 312.6 ksi | ASTM D790 |
| Izod Impact, Notched | 4.43 J/cm @Temperature -30.0 °C |
8.30 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| 5.90 J/cm @Temperature 23.0 °C |
11.1 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 260 °C | 428 - 500 °F | |
| Middle Barrel Temperature | 230 - 270 °C | 446 - 518 °F | |
| Front Barrel Temperature | 240 - 280 °C | 464 - 536 °F | |
| Nozzle Temperature | 240 - 280 °C | 464 - 536 °F | |
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Lucent Polymers CPP-110 Polypropylene Homopolymer, 10% Calcium Carbonate Filled
- Multibase Multi-Flex® D 4201 TPE Thermoplastic Elastomer
- Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled
- Chase Plastics CP Pryme® NN300HSL (COND, 50% RH) Nylon 66 (Utility Grade), Heat Stabilized, Internally Lubricated
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Varox DBPH-50 Peroxide
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.5 PHR Sulfur
- Dow AFFINITY™ PL 1840G Polyolefin Plastomer (POP)
- Overview of materials for Polycarbonate, Molded
Copyright © lookpolymers.com All Rights Reserved