LG Chemical LUPOY GN5001EF PC/ABS, Br, Cal-free flame retardant

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN5001EF PC/ABS, Br, Cal-free flame retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame RetardantApplication: Industrial / IT productCAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 61.8 MPa

@Thickness 3.20 mm
 8960 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 50 %

@Thickness 3.20 mm
 >= 50 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 99.0 MPa

@Thickness 3.20 mm
 14400 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 6.86 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 12.9 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 108 °C

@Thickness 6.40 mm
 226 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 225 - 240 °C
437 - 464 °F
Injection Molding
Middle Barrel Temperature 240 - 255 °C
464 - 491 °F
Injection Molding
Front Barrel Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Nozzle Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Melt Temperature 235 - 265 °C
455 - 509 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 0.0200 - 0.0600 MPa
2.90 - 8.70 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding