LG Chemical LUPOL TE5208 PP+Rubber+MF, High Impact
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL TE5208 PP+Rubber+MF, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 - 1.00 g/cc | 0.970 - 1.00 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm |
0.0070 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.6 MPa @Thickness 3.20 mm |
2700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 180 % @Thickness 3.20 mm |
180 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 27.0 MPa @Thickness 6.40 mm |
3910 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 1.57 GPa @Thickness 6.40 mm |
228 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.598 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
>= 1.12 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| >= 4.71 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 8.82 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polymer Resources PC-GP3-TFE5 Polycarbonate, 5% PTFE, High Flow, Wear Resistant
- ICO Polymers ICORENEâ„¢ 115-1327 LMDPE Rotational Molding Resin
- Monmouth Rubber & Plastics Durafoamâ„¢ IVN 41 NEO/PVC/NBR
- SABIC Innovative Plastics PC6300 PC (Asia Pacific)
- SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP MX88028 PP (Asia Pacific)
- Toyobo GLAMIDE® T-403 Nylon-6
- Braskem LF 0720/20 AF LLDPE Blown Film Extrusion Polyethylene
- Mallard Creek Polymers ROVENE® 4457 SBR Latex