LG Chemical LUPOL TE5007B PP+Rubber, High Impact

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	LG Chemical
Trade Name	LUPOL
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LG Chemical LUPOL TE5007B PP+Rubber, High Impact.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Injection Molding, PP+Rubber, Low Density, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia , Rear Bumper Step)Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	0.900 g/cc	0.900 g/cc	ASTM D792
Maximum Moisture Content	0.010	0.010	Injection Molding
Linear Mold Shrinkage, Flow	0.0090 - 0.010 cm/cm @Thickness 3.20 mm	0.0090 - 0.010 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 Â°C	20 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	14.7 MPa @Thickness 3.20 mm	2130 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	400 % @Thickness 3.20 mm	400 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	39.2 MPa @Thickness 6.40 mm	5690 psi @Thickness 0.252 in	10mm/min; ASTM D790
Flexural Modulus	0.735 GPa @Thickness 6.40 mm	107 ksi @Thickness 0.252 in	10mm/min; ASTM D790
Izod Impact, Notched	>= 0.981 J/cm @Thickness 6.40 mm, Temperature -10.0 Â°C	>= 1.84 ft-lb/in @Thickness 0.252 in, Temperature 14.0 Â°F	ASTM D256
	>= NB @Thickness 6.40 mm, Temperature 23.0 Â°C	>= NB @Thickness 0.252 in, Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	85.0 Â°C @Thickness 6.40 mm	185 Â°F @Thickness 0.252 in	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	190 - 210 Â°C	374 - 410 Â°F	Injection Molding
Middle Barrel Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Front Barrel Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Nozzle Temperature	210 - 230 Â°C	410 - 446 Â°F	Injection Molding
Melt Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F	Injection Molding
Drying Temperature	70.0 - 80.0 Â°C	158 - 176 Â°F	Injection Molding
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour	Injection Molding
Back Pressure	29.4 - 58.8 MPa	4260 - 8530 psi	Injection Molding
Screw Speed	30 - 60 rpm	30 - 60 rpm	Injection Molding