LG Chemical LUMILOY GN1306F Injection Molding FR Heat Resistant mPPO

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer LG Chemical
Trade Name LUMILOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMILOY GN1306F Injection Molding FR Heat Resistant mPPO.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Uses include electric/electronic parts.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ASTM D792
Water Absorption 0.3 %

@Time 86400 sec
 0.3 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.006 - 0.008 cm/cm

@Thickness 3.00 mm
 0.006 - 0.008 in/in

@Thickness 0.118 in
 ASTM D955
0.007 - 0.009 cm/cm

@Thickness 2.00 mm
 0.007 - 0.009 in/in

@Thickness 0.0787 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.007 - 0.009 cm/cm

@Thickness 3.00 mm
 0.007 - 0.009 in/in

@Thickness 0.118 in
 ASTM D955
0.008 - 0.010 cm/cm

@Thickness 2.00 mm
 0.008 - 0.010 in/in

@Thickness 0.0787 in
 ASTM D955
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 71.6 MPa

@Thickness 3.20 mm
 10400 psi

@Thickness 0.126 in
 ASTM D638
Elongation at Break 20 %

@Thickness 3.17 mm
 20 %

@Thickness 0.125 in
 ASTM D638
Flexural Strength 117 MPa

@Thickness 3.20 mm
 17000 psi

@Thickness 0.126 in
 ASTM D790
Flexural Modulus 2.45 GPa

@Thickness 3.20 mm
 356 ksi

@Thickness 0.126 in
 ASTM D790
Izod Impact, Notched 0.785 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
 1.47 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
0.981 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.84 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
1.96 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 3.67 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 135 °C

@Thickness 3.20 mm
 275 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0 - 5VA

@Thickness 2.00 mm
 V-0 - 5VA

@Thickness 0.0787 in
V-0 - 5VA

@Thickness 3.00 mm
 V-0 - 5VA

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Middle Barrel Temperature 260 - 290 °C
500 - 554 °F
Front Barrel Temperature 260 - 300 °C
500 - 572 °F
Nozzle Temperature 260 - 300 °C
500 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90 - 100 °C
190 - 212 °F
Dry Time 3 - 4 hour
3 - 4 hour
Moisture Content >= 0.01 %
>= 0.01 %