NOVA Chemicals Sclair® 11J4 Octene LLDPE Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® 11J4 Octene LLDPE Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Low gel, excellent hermetic heat sealability, easy processability, high toughness and strength.Applications: Sealant web in food packaging, vacuum packaging, barrier applications, etc.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in³	ASTM D792
Melt Flow	0.95 g/10 min @Load 2.16 kg, Temperature 190 °C	0.95 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.50 MPa	1380 psi	ASTM D882
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Film Elongation at Break, MD	640 %	640 %	ASTM D882
Film Elongation at Break, TD	770 %	770 %	ASTM D882
Secant Modulus, MD	0.190 GPa	27.6 ksi	ASTM D882
Secant Modulus, TD	0.200 GPa	29.0 ksi	ASTM D882
Coefficient of Friction	0.15	0.15	ASTM D1894
Elmendorf Tear Strength, MD	18.0 g/micron	457 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	24.0 g/micron	610 g/mil	ASTM D1922
Dart Drop	7.00 g/micron	178 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	35.0 MPa	5080 psi	ASTM D882
Film Tensile Strength at Break, TD	33.0 MPa	4790 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	12 % @Thickness 0.0250 mm	12 % @Thickness 0.000984 in	ASTM D1003
Gloss	50 %	50 %	45°; 1 mil; ASTM D1894

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 230 °C	428 - 446 °F