LG Chemical LUCON PO-5300M Electrically Conductive Thermoplastic
| Category | Polymer , Thermoplastic |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON PO-5300M Electrically Conductive Thermoplastic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solving problems associated with build-up of electrostatic charges, electrostatic discharge, and electromagnetic interference. These materials span the surface resistivity spectrum from antistatic through conductive to EMI shielding (100-1012O).Applications: I.C. tray, wafer carrier, I.C. magazine, notebook PC case, home appliance part, LCD cassette trayInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 87 | 87 | ASTM D785 |
| Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | <= 10 % | <= 10 % | ASTM D638 |
| Flexural Strength | 157 MPa | 22800 psi | ASTM D790 |
| Flexural Modulus | 9.81 GPa | 1420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | >= 0.250 W/m-K | >= 1.74 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 1.00e+6 ohm-cm | 1e+05 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 - 1.00e+6 ohm | 1e+05 - 1.00e+6 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 300 - 350 °C | 572 - 662 °F | |
| Middle Barrel Temperature | 300 - 350 °C | 572 - 662 °F | |
| Front Barrel Temperature | 300 - 350 °C | 572 - 662 °F | |
| Nozzle Temperature | 300 - 350 °C | 572 - 662 °F | |
| Melt Temperature | 310 - 360 °C | 590 - 680 °F | |
| Mold Temperature | 80.0 - 150 °C | 176 - 302 °F | |
| Drying Temperature | 110 - 120 °C | 230 - 248 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 49.03 - 78.45 MPa | 7111 - 11380 psi | Second |
| 58.8 - 118 MPa | 8530 - 17100 psi | First | |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 455 Carboxylated Styrene - Butadiene Copolymer
- SABIC PP 524P Polypropylene Homopolymer for Bi-axially Oriented Film
- SABIC Innovative Plastics Lexan® BM5225X PC (Asia Pacific)
- KaMin Polyplate® P Kaolin Clay - Delaminated
- H.C. Starck HPM 1705 Tungsten High Density Composite
- Karina E 02/127-FC-LMP Yellow Color Concentrate for PVC
- Techmer ES Plaslube® NY-1/MS/5 NAT PA66
- DuPont Performance Polymers Zytel® HTN 92G35DH2 BK083 Polyphthalamide (PPA) (Unverified Data**)
- Dow Nordel® IP 5565 ASTM D3568
- E-Polymers TEKAFIN® PH50GM 30% Glass Fiber Reinforced Mineral Filled Low Warpage Compounded-PP
Copyright © lookpolymers.com All Rights Reserved