Quadrant EPP Duratron® PAI T7530, Compression Molded Carbon Fiber Reinforced Polyamide-Imide
| Category | Polymer , Thermoplastic , Polyamide-imide (PAI) |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Duratron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Duratron® PAI T7530, Compression Molded Carbon Fiber Reinforced Polyamide-Imide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc @Temperature 22.8 °C |
1.51 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Water Absorption at Saturation | 1.5 % | 1.5 % | ASTM D570 2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 90 | 90 | ASTM D785 |
| Tensile Strength | 86.2 MPa @Temperature 22.8 °C |
12500 psi @Temperature 73.0 °F |
ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Tensile Modulus | 5.03 GPa @Temperature 22.8 °C |
730 ksi @Temperature 73.0 °F |
ASTM D638 |
| Flexural Strength | 124 MPa @Temperature 22.8 °C |
18000 psi @Temperature 73.0 °F |
ASTM D790 |
| Flexural Modulus | 6.89 GPa @Temperature 22.8 °C |
1000 ksi @Temperature 73.0 °F |
ASTM D790 |
| Compressive Strength | 296 MPa @Strain 10.0 %, Temperature 22.8 °C |
43000 psi @Strain 10.0 %, Temperature 73.0 °F |
ASTM D965 |
| Compressive Modulus | 6.69 GPa | 971 ksi | ASTM D695 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | Type "A"; ASTM D256 |
| Coefficient of Friction | 0.22 | 0.22 | QTM 55007 |
| K (wear) Factor | 226 x 10-8 mm³/N-M | 112 x 10-10 in³-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 1.51 MPa-m/sec | 43000 psi-ft/min | (with 4:1 safety factor applied); QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.519 W/m-K | 3.60 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
| Flammability, UL94 | V-0 | V-0 | UL94 |
Users viewing this material also viewed the following:
- Mytex Polymers AN16L-06 Polypropylene, Compounded
- Nylene® PA6/6 Impact Modified 411 HS Nylon 6/6
- Propylene Oxide Rubber (GPO)
- Lucite International Diakon® LG156 Acrylic Bead Polymer, High Transparency
- SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East)
- Lubrizol Telene 1650 A/BK Dicyclopentadiene (DCPD)
- Eagle Brass 304 Austenitic Stainless Steel, 1/8 Hardened
- Covestro Bayflex® XGT-100 Polyurethane Elastomeric RIM, 15% Milled Glass Filled, MDI-based 2-Component Liquid System
- Resirene Resirene® 6110 High Impact Polystyrene
Copyright © lookpolymers.com All Rights Reserved