LG Chemical LUCEL HI515W POM+Rubber, High Impact
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | LG Chemical |
| Trade Name | LUCEL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCEL HI515W POM+Rubber, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, POM+Rubber, High ImpactApplication: Gears, Automobile ClipCAS No. 66455-31-0 and 155123-66-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.017 - 0.020 cm/cm @Thickness 3.20 mm |
0.017 - 0.020 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 64 | 64 | ASTM D785 |
| Tensile Strength, Yield | 41.9 MPa @Thickness 3.20 mm |
6070 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 67 % @Thickness 3.20 mm |
67 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 47.3 MPa @Thickness 3.20 mm |
6860 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 1.418 GPa @Thickness 3.20 mm |
205.7 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.726 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.36 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C @Thickness 6.40 mm |
174 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding |
| Back Pressure | 0.490 - 3.04 MPa | 71.1 - 441 psi | Injection Molding |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200-30 Polyester SMC
- Palm Labs Adhesives Turbo Fuse Series 130SI Surface Insensitive (100 Viscosity) Rapid Bonding Adhesive
- Ravago Manufacturing Americas Hylex® P1025L Polycarbonate, High Flow, Mold Release
- Gromax BFG30-FH00B1 Nylon 6 30% Glass Filled (Dry)
- Borealis Daplen™ KSR4525 Polypropylene Reactor Elastomer Modified
- ExxonMobil Exxtral™ BMV 102W Performance Polyolefin
- CLAL-MSX ARCAP Anticorrosion AP4 0 Annealed, Drawn Copper Alloy
- Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded
- Lanxess Pocan® DP B 3235 XF 901510 PBT, 30% Glass Fiber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved