LG Chemical LUCEL FW700S Modified POM, Friction Resistance, Abrasion Resistance

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer LG Chemical
Trade Name LUCEL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCEL FW700S Modified POM, Friction Resistance, Abrasion Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Maximum Moisture Content 0.10
0.10
Injection Molding
Linear Mold Shrinkage, Flow 0.020 - 0.022 cm/cm

@Thickness 3.20 mm
 0.020 - 0.022 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80
80
ASTM D785
Tensile Strength, Yield 53.9 MPa

@Thickness 3.20 mm
 7820 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 70 %

@Thickness 3.20 mm
 70 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 78.5 MPa

@Thickness 3.20 mm
 11400 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.883 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 155 °C

@Thickness 6.40 mm
 311 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C

@Thickness 6.40 mm
 221 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 50.0 °C

@Thickness 0.950 - 2.90 mm
 122 °F

@Thickness 0.0374 - 0.114 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 0.950 - 2.90 mm
 122 °F

@Thickness 0.0374 - 0.114 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 0.950 - 2.90 mm
 122 °F

@Thickness 0.0374 - 0.114 in
Flammability, UL94 HB

@Thickness >=0.950 mm
 HB

@Thickness >=0.0374 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 160 - 180 °C
320 - 356 °F
Injection Molding
Middle Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Front Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Nozzle Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Melt Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Injection Molding
Drying Temperature 90.0 - 110 °C
194 - 230 °F
Injection Molding
Dry Time 2.00 - 3.00 hour
2.00 - 3.00 hour
Injection Molding
Back Pressure 0.490 - 3.04 MPa
71.1 - 441 psi
Injection Molding
Screw Speed 50 - 100 rpm
50 - 100 rpm
Injection Molding