PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS)

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.52 g/cc	1.52 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.020 - 0.040 cm/cm	0.020 - 0.040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm	0.010 - 0.030 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	159 MPa	23100 psi	5.1 mm/min; ASTM D638
Tensile Strength, Yield	159 MPa	23100 psi	5.1 mm/min; ASTM D638
Elongation at Break	1.0 %	1.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	26.8 GPa	3890 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	248 MPa	36000 psi	1.3 mm/min; ASTM D790
Flexural Modulus	20.7 GPa	3000 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.590 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	1.11 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic	0.16	0.16	vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static	0.19	0.19	vs. Steel - Static; ASTM D1894

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 µm/m-°C	61.1 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	278 °C @Thickness 6.35 mm	532 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	227 °C @Thickness 6.35 mm	441 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm - 1e+05	1000 ohm-cm - 1e+05	ASTM D257
Surface Resistance	1000 ohm - 1e+05	1000 ohm - 1e+05	ASTM D257

Processing Properties	Metric	English	Comments
Drying Temperature	121 °C	250 °F
Dry Time	2.00 hour	2.00 hour

Descriptive Properties	Value	Comments
Features	Electrically Conductive
	Good Chemical Resistance
	Good Wear Resistance
	High Heat Resistance
	High Rigidity
	Linear Polymer Structure
	Lubricated
	Semi Crystalline
Forms	Pellets
Generic Material	PPS
Generic Name	Polyphenylene Sulfide (PPS)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers