LG Chemical KEYFLEX BT 3047D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 3047D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, Functional, Fast Molding, Medium ModulusApplication: Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 20.6 MPa @Thickness 2.00 mm |
2990 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 500 % @Thickness 2.00 mm |
500 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.127 GPa @Thickness 6.40 mm |
18.5 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
3.67 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 215 - 235 °C | 419 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Injection Molding |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Zone 1 | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Zone 2 | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Zone 3 | 220 - 240 °C | 428 - 464 °F | Extrusion Molding |
| Zone 4 | 225 - 245 °C | 437 - 473 °F | Extrusion Molding |
| Adapter Temperature | 225 - 245 °C | 437 - 473 °F | Extrusion Molding |
| Die Temperature | 215 - 255 °C | 419 - 491 °F | Extrusion Molding |
| Melt Temperature | 215 - 245 °C | 419 - 473 °F | Injection Molding |
| 215 - 245 °C | 419 - 473 °F | Extrusion Molding | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Plansee WC20 Cerium Oxide-doped Tungsten
- SABIC Innovative Plastics LNP LUBRICOMP PFP36 PA 6 (Asia Pacific)
- Sharadaa Ceramics REFINSUL 11LI Insulating Castables Medium/High Purity
- Toyobo Diaflora® BD 2080B
- Teknor Apex Telcar® TL-1934F Styrenic Thermoplastic Elastomer
- A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
- Chengdu Polyster 8500 General Grade TPV
- Calsak CS-72L General Purpose ABS Resin
- Polimeri Europa EDISTIR SRL550 High Impact Polystyrene (HIPS) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved