LG Chemical HG-174 ABS, High Gloss, Super High Flow

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical HG-174 ABS, High Gloss, Super High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by LG Chem
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ISO 2577
Melt Index of Compound 56.7 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 56.7 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break 18 %
18 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 76.0 MPa
11000 psi
2 mm/min; ISO 178
Flexural Modulus 2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
13.0 kJ/m²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 ISO 80
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear 97.0 µm/m-°C

@Temperature 20.0 °C
 53.9 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
CTE, linear, Transverse to Flow 94.0 µm/m-°C

@Temperature 20.0 °C
 52.2 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C
207 °F
Annealed, 80°C, 4 hours; ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Annealed, 80°C, 4 hours; ISO 175
Vicat Softening Point 95.0 °C
203 °F
50 N, 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 93
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 93
Dielectric Constant 2.8

@Frequency 1e+6 Hz
 2.8

@Frequency 1e+6 Hz
 IEC 250
2.9

@Frequency 100 Hz
 2.9

@Frequency 100 Hz
 IEC 250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 243
Dissipation Factor 0.0090

@Frequency 1e+6 Hz
 0.0090

@Frequency 1e+6 Hz
 IEC 250
Comparative Tracking Index 575 V
575 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 220 - 250 °C
428 - 482 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying