LG Chemical AF312C ABS, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical AF312C ABS, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 79-94-7 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 53 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 53 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 103
103
ASTM D785
Tensile Strength, Yield 42.2 MPa

@Thickness 3.20 mm
 6120 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Tensile Modulus 2.16 GPa

@Thickness 3.20 mm
 313 ksi

@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 70.6 MPa

@Thickness 6.40 mm
 10200 psi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 6.40 mm
 370 ksi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.45 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 4.59 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
2.45 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.59 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.785 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.785 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 84.0 °C

@Thickness 6.40 mm
 183 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C

@Thickness 6.40 mm
 169 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
84.0 °C

@Thickness 6.40 mm
 183 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 84.0 °C

@Load 5.00 kg
 183 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 70.0 °C
158 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-0

@Thickness >=2.50 mm
 V-0

@Thickness >=0.0984 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 0.490 - 0.981 MPa
71.1 - 142 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding