LATI Latistat 66-06 PA66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	LATI
Trade Name	Latistat
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latistat 66-06 PA66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Dissipative product based on Polyamide 66 (PA66). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.20 g/cc	0.0434 lb/inÂ³
Linear Mold Shrinkage, Flow	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.0125 - 0.0155 cm/cm	0.0125 - 0.0155 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	75.0 MPa	10900 psi
Elongation at Break	2.7 %	2.7 %
Tensile Modulus	3.70 GPa	537 ksi
Charpy Impact Unnotched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Charpy Impact, Notched	0.300 J/cmÂ²	1.43 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	230 Â°C	446 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	100 Â°C	212 Â°F
Vicat Softening Point	245 Â°C @Load 5.00 kg	473 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	4000 ohm-cm	4000 ohm-cm
Surface Resistance	350 ohm	350 ohm

Processing Properties	Metric	English
Melt Temperature	270 - 300 Â°C	518 - 572 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa