LATI Latistat 63-08 PA6, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer LATI
Trade Name Latistat
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latistat 63-08 PA6, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dissipative product based on Polyamide 6 (PA6), impact modified. Unfilled.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
Linear Mold Shrinkage, Flow 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Linear Mold Shrinkage, Transverse 0.0125 - 0.015 cm/cm
0.0125 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Elongation at Break 80 %
80 %
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 2.20 GPa
319 ksi
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 170 °C

@Load 5.00 kg
338 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 1.50e+8 ohm
1.50e+8 ohm
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 60.0 - 70.0 °C
140 - 158 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa