LATI Latimass 47/7-04 D008 PP Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	LATI
Trade Name	Latimass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 47/7-04 D008 PP Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Polypropylene copolymer (PPc). Special filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	0.780 g/cc	0.0282 lb/in³
Linear Mold Shrinkage, Flow	0.0070 - 0.011 cm/cm	0.0070 - 0.011 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.011 cm/cm	0.0070 - 0.011 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	8.00 MPa	1160 psi
Elongation at Break	2.0 %	2.0 %
Elongation at Yield	1.0 %	1.0 %
Tensile Modulus	1.05 GPa	152 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F
Vicat Softening Point	95.0 °C @Load 5.00 kg	203 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	180 - 200 °C	356 - 392 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F
Drying Temperature	70.0 - 90.0 °C @Time 10800 sec	158 - 194 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa