SABIC Innovative Plastics LNP Thermotuf PF007IX2 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermotuf PF007IX2 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP * THERMOTUF* PF007IX2 is a compound based on PA 6 resin containing Glass Fiber. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 171 MPa | 24800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 122 µm/m-°C @Temperature 23.0 - 60.0 °C |
67.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF50 - TPU Rigid Thermoplastic Polyurethane, 50% Long Glass Fiber Reinforced
- Polimeri Europa Eraclene® MP 90 High Density Polyethylene - Injection Molding
- H.C. Starck Amperit® 568.062 Tungsten Carbide-Nickel 92-8 - Nickel SF RC 60 65-35
- H.C. Starck Amperit® 832.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Latrobe Lescalloy® 300M VAC-ARC High Strength Alloy Steel
- Hexcel® HexForce™ 4700 Fiber Glass Fabric
- Braskem TN2006 EVA General Film Copolymer
- Multibase Multi-Flam™ 0102 PP NH Polypropylene
- BASF Lupranate® 278 Isocyanate
Copyright © lookpolymers.com All Rights Reserved