LATI Latamid 12 H 90FE03 PA 12, Heat Stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latamid
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latamid 12 H 90FE03 PA 12, Heat Stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyamide 12 (PA12) based compound. Heat stabilized. Magnetizable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	4.50 g/cc	0.163 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm	0.0060 - 0.0080 in/in
Linear Mold Shrinkage, Transverse	0.0060 - 0.0080 cm/cm	0.0060 - 0.0080 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	40.0 MPa	5800 psi
Elongation at Break	0.60 % @Temperature 23.0 Â°C	0.60 % @Temperature 73.4 Â°F
Tensile Modulus	13.3 GPa	1930 ksi
Charpy Impact Unnotched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²
Charpy Impact, Notched	0.100 J/cmÂ²	0.476 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	150 Â°C	302 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	95.0 Â°C	203 Â°F
Vicat Softening Point	160 Â°C @Load 5.00 kg	320 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	250 - 270 Â°C	482 - 518 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	70.0 - 90.0 Â°C @Time 10800 sec	158 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa