LATI Latilub 95-25GR CE/10 PSU, Mineral Fiber Reinforced, Graphite Filled

Category Polymer , Thermoplastic , Polyarylsulfone (PAS) , Polyarylsulfone; Molded/Extruded
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 95-25GR CE/10 PSU, Mineral Fiber Reinforced, Graphite Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polysulfone (PSU). Graphite. Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0080 cm/cm
0.0055 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
Elongation at Break 1.2 %
1.2 %
Tensile Modulus 8.50 GPa
1230 ksi
Charpy Impact Unnotched 1.00 J/cm²
4.76 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Coefficient of Friction, Dynamic 0.18
0.18
Coefficient of Friction, Static 0.23
0.23
K (wear) Factor 12.0 x 10-8 mm³/N-M
5.96 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Vicat Softening Point 180 °C

@Load 5.00 kg
356 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 300 - 330 °C
572 - 626 °F
Mold Temperature 100 - 120 °C
212 - 248 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa