LATI Latilon 28D-V0 PC, Flame Retardant

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer LATI
Trade Name Latilon
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilon 28D-V0 PC, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate (PC) based compound. UL94 V-0 classified, brominated and chlorinated halogens-based flame retardants free. Low smoke density and low toxicity index. Very high dimensional stability. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
Linear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 23.0 MPa

@Temperature 120 °C
 3340 psi

@Temperature 248 °F
25.0 MPa

@Temperature 90.0 °C
 3630 psi

@Temperature 194 °F
30.0 MPa

@Temperature 60.0 °C
 4350 psi

@Temperature 140 °F
50.0 MPa

@Temperature 23.0 °C
 7250 psi

@Temperature 73.4 °F
Elongation at Break 70 %

@Temperature 60.0 °C
 70 %

@Temperature 140 °F
80 %

@Temperature 23.0 °C
 80 %

@Temperature 73.4 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
Elongation at Yield 2.5 %

@Temperature 120 °C
 2.5 %

@Temperature 248 °F
3.0 %

@Temperature 90.0 °C
 3.0 %

@Temperature 194 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
Tensile Modulus 1.60 GPa

@Temperature 120 °C
 232 ksi

@Temperature 248 °F
1.80 GPa

@Temperature 90.0 °C
 261 ksi

@Temperature 194 °F
2.10 GPa

@Temperature 60.0 °C
 305 ksi

@Temperature 140 °F
2.40 GPa

@Temperature 23.0 °C
 348 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
 284 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Oxygen Index 37 %
37 %
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 200 V
200 V
A solution
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa