DuPont Performance Polymers Hytrel® HTR8441 BK316 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Hytrel® HTR8441 BK316 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
55 Shore D High Viscosity Polyester Elastomer Developed for Blow MoldingInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
1.19 g/cc
0.0430 lb/in³
ISO 1183
Viscosity 114600 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 114600 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
143100 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 230 °C
 143100 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 446 °F
 ISO 11403-1 -2
511800 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 511800 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
643200 cP
<br>@Shear Rate 500 1/s,<br> Temperature 230 °C
 643200 cP
<br>@Shear Rate 500 1/s,<br> Temperature 446 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.022 cm/cm
0.022 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ISO 294-4 2577
Melt Flow 10 g/10 min
<br>@Load 10.0 kg,<br> Temperature 240 °C
 10 g/10 min
<br>@Load 22.0 lb,<br> Temperature 464 °F
 cm³/10min; ISO 1133
10 g/10 min
<br>@Load 10.0 kg,<br> Temperature 240 °C
 10 g/10 min
<br>@Load 22.0 lb,<br> Temperature 464 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
15s; ISO 868
<= 58
<= 58
ISO 868
Tensile Strength at Break 35.0 MPa
5080 psi
ISO 527-1/-2
Tensile Stress 7.80 MPa
<br>@Strain 5.00 %
 1130 psi
<br>@Strain 5.00 %
 ISO 527-1/-2
11.9 MPa
<br>@Strain 10.0 %
 1730 psi
<br>@Strain 10.0 %
 ISO 527-1/-2
19.0 MPa
<br>@Strain 50.0 %
 2760 psi
<br>@Strain 50.0 %
 ISO 527-1/-2
4.57 MPa
<br>@Strain 13.22 %,<br> Temperature 150 °C
 663 psi
<br>@Strain 13.22 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
5.83 MPa
<br>@Strain 11.72 %,<br> Temperature 120 °C
 846 psi
<br>@Strain 11.72 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
5.87 MPa
<br>@Strain 30.75 %,<br> Temperature 150 °C
 851 psi
<br>@Strain 30.75 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
6.51 MPa
<br>@Strain 48.57 %,<br> Temperature 150 °C
 944 psi
<br>@Strain 48.57 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
7.05 MPa
<br>@Strain 66.04 %,<br> Temperature 150 °C
 1020 psi
<br>@Strain 66.04 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
7.55 MPa
<br>@Strain 82.79 %,<br> Temperature 150 °C
 1100 psi
<br>@Strain 82.79 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
7.69 MPa
<br>@Strain 12.63 %,<br> Temperature 90.0 °C
 1120 psi
<br>@Strain 12.63 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
7.73 MPa
<br>@Strain 28.06 %,<br> Temperature 120 °C
 1120 psi
<br>@Strain 28.06 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
7.96 MPa
<br>@Strain 8.44 %,<br> Temperature 60.0 °C
 1150 psi
<br>@Strain 8.44 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
8.14 MPa
<br>@Strain 99.21 %,<br> Temperature 150 °C
 1180 psi
<br>@Strain 99.21 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
8.62 MPa
<br>@Strain 44.89 %,<br> Temperature 120 °C
 1250 psi
<br>@Strain 44.89 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
8.69 MPa
<br>@Strain 114.16 %,<br> Temperature 150 °C
 1260 psi
<br>@Strain 114.16 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
9.20 MPa
<br>@Strain 128.33 %,<br> Temperature 150 °C
 1330 psi
<br>@Strain 128.33 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
9.32 MPa
<br>@Strain 61.46 %,<br> Temperature 120 °C
 1350 psi
<br>@Strain 61.46 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
9.45 MPa
<br>@Strain 8.11 %,<br> Temperature 40.0 °C
 1370 psi
<br>@Strain 8.11 %,<br> Temperature 104 °F
 TPE; ISO 11403-1 -2
9.69 MPa
<br>@Strain 141.75 %,<br> Temperature 150 °C
 1410 psi
<br>@Strain 141.75 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
9.95 MPa
<br>@Strain 77.39 %,<br> Temperature 120 °C
 1440 psi
<br>@Strain 77.39 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
10.0 MPa
<br>@Strain 29.16 %,<br> Temperature 90.0 °C
 1450 psi
<br>@Strain 29.16 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
10.39 MPa
<br>@Strain 160.99 %,<br> Temperature 150 °C
 1507 psi
<br>@Strain 160.99 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
10.75 MPa
<br>@Strain 97.58 %,<br> Temperature 120 °C
 1559 psi
<br>@Strain 97.58 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
10.83 MPa
<br>@Strain 173.83 %,<br> Temperature 150 °C
 1571 psi
<br>@Strain 173.83 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
11.09 MPa
<br>@Strain 46.26 %,<br> Temperature 90.0 °C
 1608 psi
<br>@Strain 46.26 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
11.37 MPa
<br>@Strain 189.93 %,<br> Temperature 150 °C
 1649 psi
<br>@Strain 189.93 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
11.46 MPa
<br>@Strain 116.58 %,<br> Temperature 120 °C
 1662 psi
<br>@Strain 116.58 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
11.96 MPa
<br>@Strain 62.83 %,<br> Temperature 90.0 °C
 1735 psi
<br>@Strain 62.83 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
12.07 MPa
<br>@Strain 213.35 %,<br> Temperature 150 °C
 1751 psi
<br>@Strain 213.35 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
12.07 MPa
<br>@Strain 24.82 %,<br> Temperature 60.0 °C
 1751 psi
<br>@Strain 24.82 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
12.09 MPa
<br>@Strain 8.07 %,<br> Temperature 23.0 °C
 1754 psi
<br>@Strain 8.07 %,<br> Temperature 73.4 °F
 TPE; ISO 11403-1 -2
12.11 MPa
<br>@Strain 134.44 %,<br> Temperature 120 °C
 1756 psi
<br>@Strain 134.44 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
12.69 MPa
<br>@Strain 151.11 %,<br> Temperature 120 °C
 1841 psi
<br>@Strain 151.11 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
12.74 MPa
<br>@Strain 78.74 %,<br> Temperature 90.0 °C
 1848 psi
<br>@Strain 78.74 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
12.8 MPa
<br>@Strain 240.5 %,<br> Temperature 150 °C
 1860 psi
<br>@Strain 240.5 %,<br> Temperature 302 °F
 TPE; ISO 11403-1 -2
13.45 MPa
<br>@Strain 174.3 %,<br> Temperature 120 °C
 1951 psi
<br>@Strain 174.3 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
13.57 MPa
<br>@Strain 42.36 %,<br> Temperature 60.0 °C
 1968 psi
<br>@Strain 42.36 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
13.7 MPa
<br>@Strain 99.16 %,<br> Temperature 90.0 °C
 1990 psi
<br>@Strain 99.16 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
13.9 MPa
<br>@Strain 188.83 %,<br> Temperature 120 °C
 2020 psi
<br>@Strain 188.83 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
14.24 MPa
<br>@Strain 24.71 %,<br> Temperature 40.0 °C
 2065 psi
<br>@Strain 24.71 %,<br> Temperature 104 °F
 TPE; ISO 11403-1 -2
14.45 MPa
<br>@Strain 207.18 %,<br> Temperature 120 °C
 2096 psi
<br>@Strain 207.18 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
14.55 MPa
<br>@Strain 118.91 %,<br> Temperature 90.0 °C
 2110 psi
<br>@Strain 118.91 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
14.65 MPa
<br>@Strain 59.7 %,<br> Temperature 60.0 °C
 2125 psi
<br>@Strain 59.7 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
15.1 MPa
<br>@Strain 234.77 %,<br> Temperature 120 °C
 2190 psi
<br>@Strain 234.77 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
15.31 MPa
<br>@Strain 137.97 %,<br> Temperature 90.0 °C
 2221 psi
<br>@Strain 137.97 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
15.61 MPa
<br>@Strain 76.42 %,<br> Temperature 60.0 °C
 2264 psi
<br>@Strain 76.42 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
15.63 MPa
<br>@Strain 270.58 %,<br> Temperature 120 °C
 2267 psi
<br>@Strain 270.58 %,<br> Temperature 248 °F
 TPE; ISO 11403-1 -2
15.83 MPa
<br>@Strain 42.79 %,<br> Temperature 40.0 °C
 2296 psi
<br>@Strain 42.79 %,<br> Temperature 104 °F
 TPE; ISO 11403-1 -2
15.98 MPa
<br>@Strain 156.09 %,<br> Temperature 90.0 °C
 2318 psi
<br>@Strain 156.09 %,<br> Temperature 194 °F
 TPE; ISO 11403-1 -2
16.78 MPa
<br>@Strain 97.74 %,<br> Temperature 60.0 °C
 2434 psi
<br>@Strain 97.74 %,<br> Temperature 140 °F
 TPE; ISO 11403-1 -2
16.82 MPa
<br>@Strain 9.10 %,<br> Temperature 0.000 °C
 2440 psi
<br>@Strain 9.10 %,<br> Temperature 32.0 °F
 TPE; ISO 11403-1 -2