LATI Latigray 82-03 CW/96 F3 PA 12, Metallic Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latigray
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 82-03 CW/96 F3 PA 12, Metallic Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polyamide 12 (PA12). Metallic filler. Potentially suitable for food/medical contact application. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	10.85 g/cc	0.3920 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0050 - 0.0090 cm/cm	0.0050 - 0.0090 in/in
Linear Mold Shrinkage, Transverse	0.0050 - 0.0090 cm/cm	0.0050 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	40.0 MPa	5800 psi
Elongation at Break	0.80 %	0.80 %
Tensile Modulus	8.90 GPa	1290 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.700 J/cmÂ²	3.33 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	160 Â°C	320 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	105 Â°C	221 Â°F
Vicat Softening Point	165 Â°C @Load 5.00 kg	329 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	800 ohm-cm	800 ohm-cm
Surface Resistance	80 ohm	80 ohm

Processing Properties	Metric	English
Melt Temperature	250 - 270 Â°C	482 - 518 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
Electromagnetic reflection	95 dB
ISO Shrinkage - Pressure	60 MPa