LATI Latigray 52/11-01 CX/70 PP Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LATI
Trade Name	Latigray
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 52/11-01 CX/70 PP Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polypropylene homopolymer (PPh). Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.97 g/cc	0.0712 lb/inÂ³
Linear Mold Shrinkage, Flow	0.010 - 0.015 cm/cm	0.010 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.010 - 0.015 cm/cm	0.010 - 0.015 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	20.0 MPa	2900 psi
Elongation at Break	1.2 %	1.2 %
Tensile Modulus	2.90 GPa	421 ksi
Charpy Impact Unnotched	0.700 J/cmÂ²	3.33 ft-lb/inÂ²
Charpy Impact, Notched	0.130 J/cmÂ²	0.619 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	115 Â°C	239 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	70.0 Â°C	158 Â°F
Vicat Softening Point	140 Â°C @Load 5.00 kg	284 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm

Processing Properties	Metric	English
Melt Temperature	220 - 240 Â°C	428 - 464 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa