- LATI Latigloss 66 H2 G/50 F2 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
LATI Latigloss 66 H2 G/50 F2 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Latigloss |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latigloss 66 H2 G/50 F2 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Polyamide 66 (PA66). Heat stabilized. Glass fibers. Potentially suitable for food/medical contact application. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0090 cm/cm | 0.0065 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa @Temperature 150 °C |
10200 psi @Temperature 302 °F |
|
| 95.0 MPa @Temperature 120 °C |
13800 psi @Temperature 248 °F |
||
| 125 MPa @Temperature 90.0 °C |
18100 psi @Temperature 194 °F |
||
| 175 MPa @Temperature 60.0 °C |
25400 psi @Temperature 140 °F |
||
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
||
| Elongation at Break | 2.8 % @Temperature 23.0 °C |
2.8 % @Temperature 73.4 °F |
|
| 3.2 % @Temperature 60.0 °C |
3.2 % @Temperature 140 °F |
||
| 6.7 % @Temperature 90.0 °C |
6.7 % @Temperature 194 °F |
||
| 7.5 % @Temperature 120 °C |
7.5 % @Temperature 248 °F |
||
| 8.0 % @Temperature 150 °C |
8.0 % @Temperature 302 °F |
||
| Tensile Modulus | 4.00 GPa @Temperature 150 °C |
580 ksi @Temperature 302 °F |
|
| 5.00 GPa @Temperature 120 °C |
725 ksi @Temperature 248 °F |
||
| 7.00 GPa @Temperature 90.0 °C |
1020 ksi @Temperature 194 °F |
||
| 12.0 GPa @Temperature 60.0 °C |
1740 ksi @Temperature 140 °F |
||
| 16.0 GPa @Temperature 23.0 °C |
2320 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
| Vicat Softening Point | 250 °C @Load 5.00 kg |
482 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 320 °C | 536 - 608 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7020 BLK
- PolyOne Geon™ Vinyl Flexible SL60 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Styron XZ 92059.00 Carboxylated SB
- ExxonMobil 275 NC Mobiltac
- A. Schulman POLYBATCH™ Grey 8899 Concentrate Based In Polyethylene
- Zeon Chemicals Nipol® DN2835 Nitrile Elastomer
- Loctite® Prism® 7701 Primer for Low Energy Surface Plastics
- Eurostar Starpylen MCR13S PP, 15% Carbon Fiber Filled, Injection Molded
- Bales Mold Service Dia-Clust® (Diamond-Chrome) Mold Coating
- 3M Scotchkote™ 80BG 536 Urethane Elastomer
Copyright © lookpolymers.com All Rights Reserved