LATI Later 4 G/30 PBT, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Later
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4 G/30 PBT, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0055 cm/cm
0.0030 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.013 cm/cm
0.010 - 0.013 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
50.0 MPa

@Temperature 120 °C
 7250 psi

@Temperature 248 °F
70.0 MPa

@Temperature 90.0 °C
 10200 psi

@Temperature 194 °F
85.0 MPa

@Temperature 60.0 °C
 12300 psi

@Temperature 140 °F
125 MPa

@Temperature 23.0 °C
 18100 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.2 %

@Temperature 60.0 °C
 3.2 %

@Temperature 140 °F
5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
5.5 %

@Temperature 120 °C
 5.5 %

@Temperature 248 °F
5.5 %

@Temperature 150 °C
 5.5 %

@Temperature 302 °F
Tensile Modulus 3.20 GPa

@Temperature 150 °C
 464 ksi

@Temperature 302 °F
4.10 GPa

@Temperature 120 °C
 595 ksi

@Temperature 248 °F
5.10 GPa

@Temperature 90.0 °C
 740 ksi

@Temperature 194 °F
6.90 GPa

@Temperature 60.0 °C
 1000 ksi

@Temperature 140 °F
9.50 GPa

@Temperature 23.0 °C
 1380 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
5.50 J/cm²

@Temperature -20.0 °C
 26.2 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
 419 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 23 %
23 %
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa