LATI Latene® AG9H MI/40 PP Homopolymer, 40% Mica Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Mica Filler |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® AG9H MI/40 PP Homopolymer, 40% Mica Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Mica filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.0105 cm/cm | 0.0080 - 0.0105 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 5.00 MPa @Temperature 90.0 °C |
725 psi @Temperature 194 °F |
|
| 15.0 MPa @Temperature 60.0 °C |
2180 psi @Temperature 140 °F |
||
| 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 5.0 % @Temperature 60.0 °C |
5.0 % @Temperature 140 °F |
||
| 20 % @Temperature 90.0 °C |
20 % @Temperature 194 °F |
||
| Elongation at Yield | 2.0 % @Temperature 23.0 °C |
2.0 % @Temperature 73.4 °F |
|
| 3.0 % @Temperature 60.0 °C |
3.0 % @Temperature 140 °F |
||
| 3.5 % @Temperature 90.0 °C |
3.5 % @Temperature 194 °F |
||
| Tensile Modulus | 1.20 GPa @Temperature 90.0 °C |
174 ksi @Temperature 194 °F |
|
| 2.50 GPa @Temperature 60.0 °C |
363 ksi @Temperature 140 °F |
||
| 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
|
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
||
| Charpy Impact, Notched | 0.100 J/cm² @Temperature -20.0 °C |
0.476 ft-lb/in² @Temperature -4.00 °F |
|
| 0.150 J/cm² @Temperature 23.0 °C |
0.714 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 110 °C @Load 5.00 kg |
230 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nitriflex NP-2174 Powdered Nitrile
- NOVA Chemicals EPS 34RC Regular Expandable Polystyrene
- PTS Tristar® PC-10FRN (V) 15 MFI, 5VA, Flame Retardant, UV Stabilized Polycarbonate With Release
- Indium Corp. Indalloy 36 Bismuth Solder Alloy
- ITW Plexus Plexusâ„¢ MA420FS Methacrylate Adhesive
- Heatbath/Park Wire Annealing Quenching and Tempering Salt
- SABIC Innovative Plastics LNP STAT-KON DE0026 PC (Europe-Africa-Middle East)
- Teknor Apex Monprene® MP-2156-L1 Thermoplastic Elastomer
- Solvay Specialty Polymers Catalyst CT/2-OR UV Polyolefin
- Arkema Group Pebax® 2533 SA 01 MED Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved