LATI Latene® 7H2W-V0 PP Homopolymer, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® 7H2W-V0 PP Homopolymer, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
Linear Mold Shrinkage, Flow 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
Elongation at Break 20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
>= 10 %

@Temperature 60.0 °C
 >= 10 %

@Temperature 140 °F
>= 10 %

@Temperature 90.0 °C
 >= 10 %

@Temperature 194 °F
Tensile Modulus 0.500 GPa

@Temperature 90.0 °C
 72.5 ksi

@Temperature 194 °F
0.800 GPa

@Temperature 60.0 °C
 116 ksi

@Temperature 140 °F
1.80 GPa

@Temperature 23.0 °C
 261 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.0800 J/cm²

@Temperature -20.0 °C
 0.381 ft-lb/in²

@Temperature -4.00 °F
0.200 J/cm²

@Temperature 23.0 °C
 0.952 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 100 °C

@Load 5.00 kg
 212 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 33 %
33 %
Glow Wire Test 825 °C

@Thickness 1.00 mm
 1520 °F

@Thickness 0.0394 in
 GWIT
825 °C

@Thickness 2.00 mm
 1520 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa