LATI Latan 2 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | LATI |
| Trade Name | Latan |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latan 2 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyoxymethylene (POM). Unfilled. High viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.020 - 0.023 cm/cm | 0.020 - 0.023 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0205 - 0.0225 cm/cm | 0.0205 - 0.0225 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | |
| Elongation at Break | 80 % @Temperature 23.0 °C |
80 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 10 % | 10 % | |
| Tensile Modulus | 1.00 GPa @Temperature 90.0 °C |
145 ksi @Temperature 194 °F |
|
| 1.50 GPa @Temperature 60.0 °C |
218 ksi @Temperature 140 °F |
||
| 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 175 - 200 °C | 347 - 392 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer (Europe-Africa-Middle East)
- NOVA Chemicals Surpass® FPs021-F Octene sLLDPE Film Resin, 25 Micron Film
- Poco Graphite AXF-5Q10W Biomedical Grade Graphite
- Abatron 80067 A/B Filled Potting Compound (discontinued **)
- Huntsman PE1504 EVA Film Extrusion (discontinued **)
- Toyobo GLAMIDE® NB-5620S Nylon/Olefin
- China Tungsten Kmo51-B Molybdenum Concentrate
- ATI Allvac® VascoMax® T-200 Specialty Steel
- Radici Radilon® S CV300 (cond.) Nylon 6
- BP Amoco Acctuf® 3541 Impact Copolymer Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved