PolyOne Stat-Tech™ AS-15CP/000 ABS - 15% Carbon Powder (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-15CP/000 ABS - 15% Carbon Powder
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm |
0.0040 - 0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 - 0.480 J/cm @Thickness 6.35 mm |
0.599 - 0.899 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | Stock |
| Mold Temperature | 82.0 - 93.0 °C | 180 - 199 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Molding M4825 Polyvinyl Chloride, Rigid (PVC, Rigid)
- S&E Specialty Polymers G-04-036ESD PVC
- Nilit FRIANYL A63 H-SG50 Nylon 6.6 for injection molding, 50% mineral filled
- Plastcom SLOVAMID 6 GF 15 HI PA6, 15% glass fibre, improved strength
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC
- Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n
- Kazanorgsintez 102-21 Composition of Low Density Polyethylene, Crack-Proof
- LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant
- ChevronTexaco Regal® EP 32
- Adell WL-38 40% Glass and Mineral Reinforced PET
Copyright © lookpolymers.com All Rights Reserved