Eurotec® Tecomid® NBX0 GR60 NL PA6, 60% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NBX0 GR60 NL PA6, 60% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.20 % @Temperature 23.0 °C |
1.20 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 225 MPa | 32600 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Vicat Softening Point | 215 °C @Load 5.10 kg |
419 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 - 270 °C | 482 - 518 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JAC35A Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs YB300 Yb2(CO3)3·xH2O Ytterbium carbonate hydrate
- Nabaltec GRANALOX® NM 9922 I Ceramic Bodies
- Albis Plastics Cellulose Acetate Butyrate B9324 (UVI, Odor Mask Added), 4% Plasticizer (discontinued **)
- Hyosung Topilene S800F PP
- Saint-Gobain Chemfab® q-GUARD® 35 Insulation Jacketing
- Elastomer Engineering Elastamide 150 Elastomer Modified RIM Nylon 6
- Arlon Thermabond® 99A60X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Teknor Apex Monprene® MP-1878 Thermoplastic Elastomer
- 3M Novec™ 7500 Engineered Fluid
Copyright © lookpolymers.com All Rights Reserved