LATI Latamid 6 H-V0 PA 6, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H-V0 PA 6, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Linear Mold Shrinkage, Flow 0.0105 - 0.014 cm/cm
0.0105 - 0.014 in/in
Linear Mold Shrinkage, Transverse 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa

@Temperature 60.0 °C
 7250 psi

@Temperature 140 °F
70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
45 %

@Temperature 60.0 °C
 45 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 0.500 GPa

@Temperature 150 °C
 72.5 ksi

@Temperature 302 °F
0.600 GPa

@Temperature 120 °C
 87.0 ksi

@Temperature 248 °F
0.800 GPa

@Temperature 90.0 °C
 116 ksi

@Temperature 194 °F
1.40 GPa

@Temperature 60.0 °C
 203 ksi

@Temperature 140 °F
3.40 GPa

@Temperature 23.0 °C
 493 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Vicat Softening Point 200 °C

@Load 5.00 kg
 392 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 36 %
36 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
A solution
Processing Properties Metric English Comments
Melt Temperature 235 - 250 °C
455 - 482 °F
Mold Temperature 70.0 - 80.0 °C
158 - 176 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa