LATI Latamid 12 H FE90 PA 12, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 12 H FE90 PA 12, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 12 (PA12) based compound. Heat stabilized. Magnetizable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.27 g/cc | 0.118 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | |
| Elongation at Break | 1.0 % @Temperature 23.0 °C |
1.0 % @Temperature 73.4 °F |
|
| Tensile Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 160 °C @Load 5.00 kg |
320 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
||
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Magnetic Maximum Energy Product, BH | 0.40 MGOe | 0.40 MGOe |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C @Time 10800 sec |
158 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coercivity (BHc - HcB) @ 20°C | 95 kA/m | |
| Intrinsic coercivity (IHc - HcJ) @ 20°C | 250 kA/m | |
| ISO Shrinkage - Pressure | 60 MPa | |
| Remanence (Br) | 125 mT |
Users viewing this material also viewed the following:
- Reltek BONDiT™ B-482 Adhesive, Sealant & Coating System
- Technetics Group Amicon™ PEEK (Unverified Data**)
- Shakespeare Isocorâ„¢ HZ73SI high viscosity PA-6
- Saint-Gobain CHR® SG33-06(R) Industrial Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- SCG Chemicals EL-Leneâ„¢ M735 Butene (C4) Rotational Molding Resin
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Dixie Clay Filler
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- ExxonMobil HDPE HD 9856B High Density Polyethylene Resin
- Atom Adhesives AA-BOND F113 Epoxy Adhesive
- Arkema Group Orgalloy® LT 4060ISH Flexible Nylon Alloy (Conditioned)
Copyright © lookpolymers.com All Rights Reserved