LATI Lastilac 11 G/10 ABS/PC, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled
Manufacturer LATI
Trade Name Lastilac
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Lastilac 11 G/10 ABS/PC, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
ABS/PC Blend (ABS/PC) based compound. Glass fibers. Good surface appearance. Good impact resistance. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
Linear Mold Shrinkage, Flow 0.0045 - 0.0065 cm/cm
0.0045 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 5.00 MPa
<br>@Temperature 120 °C
 725 psi
<br>@Temperature 248 °F
23.0 MPa
<br>@Temperature 90.0 °C
 3340 psi
<br>@Temperature 194 °F
50.0 MPa
<br>@Temperature 60.0 °C
 7250 psi
<br>@Temperature 140 °F
60.0 MPa
<br>@Temperature 23.0 °C
 8700 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.5 %
<br>@Temperature 23.0 °C
 2.5 %
<br>@Temperature 73.4 °F
3.0 %
<br>@Temperature 60.0 °C
 3.0 %
<br>@Temperature 140 °F
6.0 %
<br>@Temperature 90.0 °C
 6.0 %
<br>@Temperature 194 °F
70 %
<br>@Temperature 120 °C
 70 %
<br>@Temperature 248 °F
Elongation at Yield 2.0 %
<br>@Temperature 60.0 °C
 2.0 %
<br>@Temperature 140 °F
2.0 %
<br>@Temperature 90.0 °C
 2.0 %
<br>@Temperature 194 °F
2.0 %
<br>@Temperature 120 °C
 2.0 %
<br>@Temperature 248 °F
Tensile Modulus 1.30 GPa
<br>@Temperature 120 °C
 189 ksi
<br>@Temperature 248 °F
3.30 GPa
<br>@Temperature 90.0 °C
 479 ksi
<br>@Temperature 194 °F
3.60 GPa
<br>@Temperature 60.0 °C
 522 ksi
<br>@Temperature 140 °F
3.90 GPa
<br>@Temperature 23.0 °C
 566 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
<br>@Temperature 23.0 °C
 11.9 ft-lb/in²
<br>@Temperature 73.4 °F
3.50 J/cm²
<br>@Temperature -20.0 °C
 16.7 ft-lb/in²
<br>@Temperature -4.00 °F
Charpy Impact, Notched 1.20 J/cm²
<br>@Temperature -20.0 °C
 5.71 ft-lb/in²
<br>@Temperature -4.00 °F
1.50 J/cm²
<br>@Temperature 23.0 °C
 7.14 ft-lb/in²
<br>@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Vicat Softening Point 130 °C
<br>@Load 5.00 kg
 266 °F
<br>@Load 11.0 lb
Flammability, UL94 HB
<br>@Thickness 3.00 mm
 HB
<br>@Thickness 0.118 in
Electrical Properties Metric English Comments
Comparative Tracking Index 350 V
350 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 - 100 °C
<br>@Time 10800 sec
 176 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa