LATI Larton CE/60 PPS, 60% Mineral Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer LATI
Trade Name Larton
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton CE/60 PPS, 60% Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.87 g/cc
0.0676 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 150 °C
 4350 psi

@Temperature 302 °F
35.0 MPa

@Temperature 120 °C
 5080 psi

@Temperature 248 °F
55.0 MPa

@Temperature 90.0 °C
 7980 psi

@Temperature 194 °F
65.0 MPa

@Temperature 60.0 °C
 9430 psi

@Temperature 140 °F
70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 0.50 %

@Temperature 23.0 °C
 0.50 %

@Temperature 73.4 °F
0.80 %

@Temperature 60.0 °C
 0.80 %

@Temperature 140 °F
1.2 %

@Temperature 90.0 °C
 1.2 %

@Temperature 194 °F
1.7 %

@Temperature 120 °C
 1.7 %

@Temperature 248 °F
1.9 %

@Temperature 150 °C
 1.9 %

@Temperature 302 °F
Tensile Modulus 4.20 GPa

@Temperature 150 °C
 609 ksi

@Temperature 302 °F
7.60 GPa

@Temperature 120 °C
 1100 ksi

@Temperature 248 °F
9.10 GPa

@Temperature 90.0 °C
 1320 ksi

@Temperature 194 °F
9.90 GPa

@Temperature 60.0 °C
 1440 ksi

@Temperature 140 °F
11.5 GPa

@Temperature 23.0 °C
 1670 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 0.500 J/cm²
2.38 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Vicat Softening Point 250 °C

@Load 5.00 kg
 482 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 44 %
44 %
Electrical Properties Metric English Comments
Comparative Tracking Index 175 V
175 V
A solution
Processing Properties Metric English Comments
Melt Temperature 290 - 330 °C
554 - 626 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa